PHZF - Halogen-free flat heat shrink profile

Flat, fire resistant, halogen-free heat shrink profile for printing on your own on Partex equipment.

Product characteristics

  • Flat, thin-walled heat-shrinkable tube made of halogen-free material.
  • High resistance to low and high temperatures.
  • Very low gas emission during a fire.
  • Fireproof.
  • Shrink ratio 2:1.
  • Ideal for marking, when the space between the wires is small.
  • Ideal for heavy industrial applications.
  • Fast and cheap on-site marking using Partex printing machines.

Product properties

Material
ZEREX (Halogen free)
Print
Thermal transfer

PHZF20024

  • Diameter after shrinking
    1,2 mm
  • Diameter before shrinking
    2,4 mm
  • Shrink ratio
    2:1
  • Thickness
    0,51 mm
  • Working Temperature
    from -55 °C to 105 °C

PHZF20032

  • Diameter after shrinking
    1,6 mm
  • Diameter before shrinking
    3,2 mm
  • Shrink ratio
    2:1
  • Thickness
    0,51 mm
  • Working Temperature
    from -55 °C to 105 °C

PHZF20048

  • Diameter after shrinking
    2,4 mm
  • Diameter before shrinking
    4,8 mm
  • Shrink ratio
    2:1
  • Thickness
    0,51 mm
  • Working Temperature
    from -55 °C to 105 °C

PHZF20064

  • Diameter after shrinking
    3,2 mm
  • Diameter before shrinking
    6,4 mm
  • Shrink ratio
    2:1
  • Thickness
    0,64 mm
  • Working Temperature
    from -55 °C to 105 °C

PHZF20095

  • Diameter after shrinking
    4,8 mm
  • Diameter before shrinking
    9,5 mm
  • Shrink ratio
    2:1

PHZF20127

  • Diameter after shrinking
    6,4 mm
  • Diameter before shrinking
    12,7 mm
  • Shrink ratio
    2:1
  • Thickness
    0,64 mm
  • Working Temperature
    from -55 °C to 105 °C

PHZF20190

  • Diameter after shrinking
    9,5 mm
  • Diameter before shrinking
    19 mm
  • Shrink ratio
    2:1
  • Thickness
    0,77 mm
  • Working Temperature
    from -55 °C to 105 °C

PHZF20254

  • Diameter after shrinking
    12,7 mm
  • Diameter before shrinking
    25,4 mm
  • Shrink ratio
    2:1
  • Thickness
    0,89 mm
  • Working Temperature
    from -55 °C to 105 °C

PHZF20380

  • Diameter after shrinking
    19,1 mm
  • Diameter before shrinking
    38 mm
  • Shrink ratio
    2:1
  • Thickness
    1,02 mm
  • Working Temperature
    from -55 °C to 105 °C

PHZF20504

  • Diameter after shrinking
    25,4 mm
  • Diameter before shrinking
    50,4 mm
  • Shrink ratio
    2:1
  • Thickness
    0,97 mm
  • Working Temperature
    from -55 °C to 105 °C

PHZF30024

  • Diameter after shrinking
    0,8 mm
  • Diameter before shrinking
    2,4 mm
  • Shrink ratio
    3:1
  • Thickness
    0,53 mm
  • Working Temperature
    from -55 °C to 135 °C

PHZF30032

  • Diameter after shrinking
    1 mm
  • Diameter before shrinking
    3,2 mm
  • Shrink ratio
    3:1
  • Thickness
    0,58 mm
  • Working Temperature
    from -55 °C to 135 °C

PHZF30048

  • Diameter after shrinking
    1,6 mm
  • Diameter before shrinking
    4,8 mm
  • Shrink ratio
    3:1
  • Thickness
    0,58 mm
  • Working Temperature
    from -55 °C to 135 °C

PHZF30064

  • Diameter after shrinking
    2 mm
  • Diameter before shrinking
    6,4 mm
  • Shrink ratio
    3:1
  • Thickness
    0,63 mm
  • Working Temperature
    from -55 °C to 135 °C

PHZF30095

  • Diameter after shrinking
    3 mm
  • Diameter before shrinking
    9,5 mm
  • Shrink ratio
    3:1
  • Thickness
    0,63 mm
  • Working Temperature
    from -55 °C to 135 °C

PHZF30127

  • Diameter after shrinking
    4 mm
  • Diameter before shrinking
    12,7 mm
  • Shrink ratio
    3:1
  • Thickness
    0,68 mm
  • Working Temperature
    from -55 °C to 135 °C

PHZF30191

  • Diameter after shrinking
    6 mm
  • Diameter before shrinking
    19,1 mm
  • Shrink ratio
    3:1
  • Thickness
    0,9 mm
  • Working Temperature
    from -55 °C to 135 °C

PHZF30254

  • Diameter after shrinking
    8 mm
  • Diameter before shrinking
    25,4 mm
  • Shrink ratio
    3:1
  • Thickness
    1 mm
  • Working Temperature
    from -55 °C to 135 °C

PHZF30381

  • Diameter after shrinking
    12,7 mm
  • Diameter before shrinking
    38,1 mm
  • Shrink ratio
    3:1
  • Thickness
    1,1 mm
  • Working Temperature
    from -55 °C to 105 °C

Tutorial video for: PHZF